Projeto e caraterização de composições cerâmicas Al2O3-MgO-SiO2 com resíduos refratários do desmantelamento de fornos industriais de fundição
| datacite.subject.fos | Engenharia e Tecnologia::Engenharia Eletromecânica | por |
| dc.contributor.advisor | Silva, Abílio Manuel Pereira da | |
| dc.contributor.author | Rosa, António Anastácio Fonseca | |
| dc.date.accessioned | 2020-02-26T17:07:12Z | |
| dc.date.available | 2020-02-26T17:07:12Z | |
| dc.date.issued | 2016-11-8 | |
| dc.date.submitted | 2016-10-7 | |
| dc.description.abstract | Diversos processos tecnológicos que envolvam temperaturas elevadas, como são exemplo as indústrias do cimento, vidro, ferro e aço, requerem o acesso a matérias-primas naturais como sílica, areias de zircão, bauxite, dolomite, magnesite, grafite, entre outros. A disponibilidade destas matérias-primas concentra-se maioritariamente em países emergentes, fora da Europa, com riscos de instabilidade política e socioeconómica. Desta forma, na Europa aposta-se em tecnologias capazes de aumentar a eficiência das matérias-primas, reutilizando e reciclando cada vez mais produtos, em particular os resíduos refratários. Neste trabalho propõe-se a reutilização de resíduos refratários provenientes do desmantelamento de fornos industriais de fundição de aço. A matéria-prima (resíduo refratário) foi moída e separada em quatro classes granulométricas (d50: 37, 357, 1111 e 1292 µm), que foram descontaminadas através de um processo de separação magnética. As classes descontaminadas foram utilizadas na composição de duas misturas cerâmicas autoescoantes, A e B. Em ambas as composições foram utilizadas as três classes de maior diâmetro, como agregado da mistura. Na composição B foi ainda incluída a classe mais fina de resíduo na matriz, enquanto que a matriz A é composta apenas por matérias-primas virgens. Foram ainda projetadas duas composições, A’ e B’, a partir das primeiras de modo a terem composição química da matriz igual à do agregado. Estas quatro composições foram sinterizadas a 1300 ºC, 1450 ºC e 1550 ºC e foram comparadas as suas propriedades: mecânicas (flexão em três pontos e compressão), físicas (densidade e porosidade) e microestruturais. Finalmente, os métodos utilizados e os resultados dos ensaios foram analisados e discutidos. Concluiu-se que a composição B apresentava resistência à compressão de 30,4 MPa, módulo de rutura de 10,9 MPa e demonstrou-se resistente à corrosão até 2 mm de profundidade para a temperatura de 1350°C. | por |
| dc.description.abstract | Several technological high temperature processes, as cement, glass, iron, steel and other industries, need access to raw-materials such as silica, zircon sands, bauxite, dolomite, magnesite, graphite, among others. The availability of this raw-materials is mostly located on emerging countries outside Europe, with political and socioeconomic instability associated. Thus, in Europe, investments are being made on technologies capable of increasing raw-materials efficiency through recycling and reusing more materials, specially referent to refractories waste. This papper proposes the recycling of refractory waste from cast steel furnace dismounting. The refractory waste was grounded, and divided by granulometric classes (d50: 37, 357, 1111 e 1292 µm), which were decontaminated through a magnetic process. The decontaminated classes were used in two compositions of two self-flow ceramic mixtures, A and B. In both compositions the classes with greater diameter were used as Aggregate. In the matrix of the composition B was included the finer class of refractory waste, being the matrix of A only composed by virgin raw-materials. Two more compositions, A’ and B’, were projected based on the first two, so as to the composition of the matrix was the same as the aggregate. These four compositions were sintered ate 1300°C, 1450°C and 1550°C and their properties were compared: mechanical (three point flection mm and compression), phisics (density and porosity) and microstructural. Finally the used methods and test results were analyzed and critically discussed. It was concluded that mixture B reveals compression resistance of 30,4 MPa, modulus of rupture of 10,9 MPA and it is corrosion resistant up to 2 mm of deep at 1350°C. | eng |
| dc.identifier.tid | 202331369 | |
| dc.identifier.uri | http://hdl.handle.net/10400.6/9591 | |
| dc.language.iso | por | por |
| dc.subject | Cerâmica Refratária | por |
| dc.subject | Projeto de Misturas Cerâmicas | por |
| dc.subject | Resíduo Industrial | por |
| dc.subject | Reutilização | por |
| dc.title | Projeto e caraterização de composições cerâmicas Al2O3-MgO-SiO2 com resíduos refratários do desmantelamento de fornos industriais de fundição | por |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | por |
| rcaap.type | masterThesis | por |
| thesis.degree.name | 2º Ciclo em Engenharia Eletromecânica | por |