Publication

Monitorização da temperatura em ligantes geopoliméricos

datacite.subject.fosEngenharia e Tecnologia::Engenharia Civilpor
dc.contributor.advisorGomes, João Paulo de Castro
dc.contributor.advisorGorskí, Marcin
dc.contributor.authorLacão, Flávio Daniel Martins
dc.date.accessioned2018-07-11T15:29:52Z
dc.date.available2018-07-11T15:29:52Z
dc.date.issued2015-7-6
dc.date.submitted2015-6-8
dc.description.abstractAs lamas residuais das minas da Panasqueira são um material que apresenta características que permitem que sejam ativadas alcalinamente, pois são ricas em aluminossilicatos, formando geopolímeros que apresentam boas características físicas e mecânicas. As lamas residuais são um resíduo industrial, resultante da exploração mineira. Estas são depositadas à superfície, ano após ano, em grandes quantidades e o seu reaproveitamento leva a que se minimizem os impactos ambientais da sua deposição. Além disso, os geopolímeros apresentam-se como uma boa alternativa ao cimento Portland, que gera toneladas de CO2 todos os anos, sendo o CO2 um gás que leva ao aquecimento global e consequente efeito de estufa. Assim sendo, o presente trabalho insere-se numa perspetiva de desenvolvimento sustentável de novos materiais de construção, neste caso de novos ligantes de ativação alcalina. Apesar de virem sendo estudados há vários anos, os geopolímeros ainda não são muito utilizados na indústria, pois ainda existe algum desconhecimento da existência deste tipo de materiais, por parte da população, aliado a um custo de produção superior aos cimentos tradicionais, e ao desconhecimento de algumas partes do seu processo de formação, bem como à falta de normalização técnica para a sua utilização, o que limita a sua produção em larga escala. Assim sendo, o presente trabalho teve o objetivo de estudar o processo de ativação alcalina de geopolímeros obtidos através de lamas residuais, juntamente com vidro moído, metacaulino ou cinzas volantes, numa solução alcalina constituída por uma mistura de hidróxido de sódio e silicato de sódio, através da monitorização de temperatura interior das misturas, com a inserção de termopares no seu interior, com o objetivo de verificar os parâmetros intervenientes na reação bem como a influência que estes têm nas fases da ativação alcalina dos geopolímeros, a dissolução, a indução e a policondensação. Para se chegar a esse fim foram realizadas avaliações da influência de parâmetros como a quantidade de ativadores e concentração molar de NaOH, o volume de mistura, as diferentes misturas de precursores elaboradas, as razões molares de óxidos ideais propostas por Joseph Davidovits, a adição de regranulado de cortiça expandida e diferentes tipos de cura. Realizaram-se ainda ensaios de resistência à compressão, em algumas das misturas elaboradas.por
dc.description.abstractThe waste mud of Panasqueira mines are a material which have characteristics that allow them to be alkali-activated, once they are rich in aluminosilicates. In this way, these waste mud form geopolymers which exhibit good physical and mechanical characteristics. These materials are resulting from mining industrial waste, and they are deposited on the surface, year after year, in a large quantities. This sequential deposition cause serious environmental problems, so the waste mud reuse leads to the minimization of this negative environmental impact. Furthermore, geopolymers are presented as a good alternative to Portland cement, which generates, every year, tons of CO2, a gas that leads to global warming and consequent greenhouse effect. Therefore, this study is part of a sustainable perspective to develop new building materials, in this case, new alkali-activated binders. Geopolymers have been studied for many years, however, they are not yet widely used in industry, because the population is still unaware about this kind of material. In addition, there are some factors which limit geopolymers large-scale production, such as the fact of these being more expensive, when compared with traditional cements and the fact of the formation process not be fully understood, as well as the lack of technical normalization for the use of these materials. Thus, this work aimed the study of alkaline activation process of geopolymers. The geopolymers were obtained from the mixture of waste mud with milled glass, metakaolin or fly ashes in an alkaline solution of sodium hydroxide and sodium silicate. The activation process was evaluated by monitoring the internal temperature of the mixtures, by the insertion of thermocouples within the samples. This monitoring was made in order to understand the parameters involved in the all process and the influence that they have in the geopolymers alkaline activation, dissolution, induction and polycondensation. The parameters studied were the activators amount and the NaOH molar concentration, the mixture volume, mixtures with different precursors, the optimal oxides molar ratios, proposed by Joseph Davidovits, the addition of regranulated of expanded cork and different conditions of cure. Were also performed compressive strength tests on some developed mixtures.eng
dc.identifier.tid201638835
dc.identifier.urihttp://hdl.handle.net/10400.6/4978
dc.language.isoporpor
dc.subjectAtivaçãopor
dc.subjectGeopolímeropor
dc.subjectLamas Residuaispor
dc.subjectSensorpor
dc.subjectTemperaturapor
dc.titleMonitorização da temperatura em ligantes geopoliméricospor
dc.typemaster thesis
dspace.entity.typePublication
rcaap.rightsopenAccesspor
rcaap.typemasterThesispor
thesis.degree.nameMestrado Integrado em Engenharia Civilpor

Files

Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
4228_8081.pdf
Size:
21.69 MB
Format:
Adobe Portable Document Format