Estudo de aditivos para melhorar o desempenho da reciclagem de uma pasta kraft crua de Pinus sylvestris
| datacite.subject.fos | Engenharia e Tecnologia::Engenharia Química | por |
| dc.contributor.advisor | Vieira, Joana Magalhães Gonçalves Costa | |
| dc.contributor.advisor | Amaral, Maria Emília da Costa Cabral | |
| dc.contributor.author | Vicente, Zegri Moreno da Silva | |
| dc.date.accessioned | 2024-01-15T14:52:27Z | |
| dc.date.available | 2024-01-15T14:52:27Z | |
| dc.date.issued | 2023-11-30 | |
| dc.date.submitted | 2023-10-09 | |
| dc.description.abstract | Esta dissertação teve como objetivo o estudo de aditivos para melhorar o desempenho da reciclagem de uma pasta kraft crua de Pinus sylvestris. Os aditivos em estudo neste trabalho foram o amido catiónico (C Bond 35806 amostra industrial), bórax e a carboximetilcelulose sódica. Primeiramente procedeu-se à desintegração da pasta crua para a produção folhas de papel laboratoriais sem adição de aditivos com uma gramagem de 60 g/m2 , num total de 200 folhas iniciais. Uma parte das folhas foi submetida aos ensaios para a avaliação das suas propriedades físicas, as restantes foram novamente desintegradas para dar início aos ciclos de reciclagem cujo procedimento se repete ao longo de 5 ciclos. Em seguida iniciou-se o estudo de incorporação de aditivos, primeiro com bórax onde se considerou a percentagem de 1% e tempo de contacto com a suspensão fibrosa de 2h e 4h. De seguida preparam-se o amido catiónico a 3% e carboximetilcelulose a 5% e 10% (cujas percentagens são relativas à massa seca de fibra celulósica). Depois de preparadas as soluções dos aditivos, foram incorporadas nas suspensões de forma individual e avaliadas as propriedades papeleiras. Com base nos resultados obtidos foram estudadas as misturas 1% bórax 4 h + 3% AC, 1 % bórax 4 h + 5% CMC e 5% CMC + 3% AC aplicadas nas suspensões fibrosas, produziram-se as folhas com os aditivos e realizaram-se os ensaios de avaliação das mesmas. Este estudo permitiu selecionar dentre elas, qual a mistura com os melhores resultados nas propriedades finais do papel, sendo a mistura 5% CMC + 3% AC a selecionada. Esta mistura foi incorporada nos dois últimos ciclos de reciclagem (4º e 5º ciclos), com o objetivo de avaliar e prolongar o número de ciclos de reciclagem da pasta kraft crua de Pinus sylvestris, por meio do aumento da resistência mecânica dos papéis produzidos. | por |
| dc.description.abstract | This dissertation aimed to study additives to improve the recycling performance of raw kraft pulp from Pinus sylvestris. The additives under study in this work were cationic starch (C Bond 35806 industrial sample), borax and sodium carboxymethylcellulose. Firstly, the raw pulp was disintegrated to produce laboratory paper sheets without the addition of additives with a grammage of 60 g/m2 , in a total of 200 initial sheets. A portion of the leaves were subjected to tests to evaluate their physical properties, the remainder were disintegrated again to begin recycling cycles, the procedure being repeated over 5 cycles. Then the study of incorporating additives began, first with borax where a percentage of 1% and a contact time with the fibrous suspension of 2h and 4h were considered. Next, 3% cationic starch and 5% and 10% carboxymethylcellulose are prepared (the percentages of which are relative to the dry mass of cellulosic fiber). After the additive solutions were prepared, they were incorporated into the suspensions individually and the paper properties were evaluated. Based on the results obtained, mixtures of 1% borax 4 h + 3% AC, 1% borax 4 h + 5% CMC and 5% CMC + 3% AC applied to fibrous suspensions were studied, the sheets were produced with the additives and evaluation tests were carried out. This study made it possible to select, among them, the mixture with the best results in the final properties of the paper, with the mixture 5% CMC + 3% AC being selected. This mixture was incorporated into the last two recycling cycles (4th and 5th cycles), with the aim of evaluating and extending the number of recycling cycles of raw Pinus sylvestris kraft pulp, by increasing the mechanical resistance of the papers produced. | eng |
| dc.identifier.tid | 203463200 | |
| dc.identifier.uri | http://hdl.handle.net/10400.6/14073 | |
| dc.language.iso | por | por |
| dc.rights.uri | http://creativecommons.org/licenses/by-nc-sa/4.0/ | |
| dc.subject | Amido Catiónico | por |
| dc.subject | Bórax | por |
| dc.subject | Carboximetilcelulose | por |
| dc.subject | Papel | por |
| dc.subject | Propriedades Físicas do Papel | por |
| dc.subject | Reciclagem | por |
| dc.title | Estudo de aditivos para melhorar o desempenho da reciclagem de uma pasta kraft crua de Pinus sylvestris | por |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | por |
| rcaap.type | masterThesis | por |
| thesis.degree.name | 2º Ciclo em Química Industrial | por |